Kessler, Vadim
- Department of Molecular Sciences, Swedish University of Agricultural Sciences
Abstract
Poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) was reacted with iron ethoxide in a molar ratio of 1:2. This modified surfactant was used as a template for the synthesis of mesostructured, nanocomposite iron oxide-silica films and powders. Grazing incidence (GI)-SAXS measurements of the films showed that depending on the concentration of the surfactant wormhole-like, 2d-centered rectangular, orthorhombic and lamellar nanocomposite structures were formed. Interestingly, the mesoscopic ordering of the orthorhombic and 2d-centered rectangular pore structure is retained even after calcination at 1000 degrees C for one hour. The influence of heat treatment on the mesostructure was investigated by GI-SAXS, TEM and N(2)-sorption measurements.
Published in
MRS Online Proceedings Library
2005, volume: 847, pages: 177-182
Conference
Symposium on Organic-Inorganic Hybrid Materials held at the 2004 MRS Fall Meeting
SLU Authors
Seisenbaeva, Gulaim
- Department of Molecular Sciences, Swedish University of Agricultural Sciences
- Department of Molecular Sciences, Swedish University of Agricultural Sciences
UKÄ Subject classification
Inorganic Chemistry
Materials Chemistry
Nano Technology
Publication identifier
- DOI: https://doi.org/10.1557/PROC-847-EE9.13
- ISBN: 1-55899-795-4
Permanent link to this page (URI)
https://res.slu.se/id/publ/50539