This Article reports the influence of the protein network structure on the mechanical properties of foams produced from commercial wheat gluten using freeze-drying. Foams were produced from alkaline aqueous solutions at various gluten concentrations with or without glycerol, modified with bacterial cellulose nanosized fibers, or both. The results showed that 20 wt % glycerol was sufficient for plasticization, yielding foams with low modulus and high strain recovery. It was found that when fibers were mixed into the foams, a small but insignificant increase in elastic modulus was achieved, and the foam structure became more homogeneous. SEM indicated that the compatibility between the fibers and the matrix was good, with fibers acting as bridges in the cell walls. IR spectroscopy and SE-HPLC revealed a relatively low degree of aggregation, which was highest in the presence of glycerol. Confocal laser scanning microscopy revealed distinct differences in HMW-glutenin subunits and gliadin distributions for all of the different samples.

Publicerad i

Biomacromolecules
2011, Volym: 12, nummer: 5, sidor: 1707-1715
Utgivare: AMER CHEMICAL SOC

SLU författare

• Johansson, Eva

  • Institutionen för biosystem och teknologi, Sveriges lantbruksuniversitet
    

UKÄ forskningsämne

Livsmedelsvetenskap


Publikationens identifierare

DOI: https://doi.org/10.1021/bm200067f

Permanent länk till denna sida (URI)

https://res.slu.se/id/publ/58897